Avaliação histométrica e histoquímica de vidro bioativo no processo de reparação óssea

Abstract

The autogenous origin grafts are osteogenic and have the advantage of producing bone tissue originated from the body itself. Its limitation is the great surgical morbidity. The bioglass is a bioactive ceramic with unlimited availability that leads to a surgery with less morbidity. This study aimed to evaluate the bioglass test during bone repair and to compare it with other bone substitutes in experimental surgical defects in the tibia of rats. The bioglass test (CEELBIO, Belo Horizonte, Brazil), has been characterized and compared to the Biogran® (Biomet 3i Inovattions Inc., Palm Beach Gardens, USA) by spectroscopy in the infrared, scanning electron microscopy (SEM), EDS spectroscopy and Rx fluorescence. The study in vivo has been started after the structural analysis. 120 rats (Rattus norvegicus albinus, Wistar rats), with approximately 7 to 8 weeks, were used. The bone defects were performed in the right tibia of animals and filled according to the following breakdown: Group I- negative control without filling; Group II- filled by Biogran®; Group III- filled with bioglass test; IV- positive control group, with filling of autogenous bone. At 7, 14, 21, 28, 49 and 70 postoperative days, the animals were euthanized and bone mineralization processes and repair were analyzed by histomorphometry (% of newly formed bone in the defect site). BMP-2 levels were measured by ELISA assay. Statistical analysis was performed using SPSS (version 20.0, SPSS Inc., Chicago, USA). The results of the histological analysis showed that in the negative control there was no bone growth up to 14 days (20.40%, p <0.001) and after reabsorption, within 21 days (6.60%, p <0.001). In Biogran® group, there was new bone formation along the grain in 7 days (34.20%, p = 0.019) and that was maintained as the material was present in shortcomings in 70 days (15.67%, p = 0.048) . The test bioglass was completely reabsorbed within 21 days; new bone formation and peaks were observed in 7 (21.00%, p = 0.019) and 49 days (15.60%, p = 0.036). In this group, macrophage-like cells arranged in sheets, were viewed with the newly formed bone. On the positive control, autologous bone was completely reabsorbed within 14 days, and the peak bone formation occurred at the same moment, within 14 days (40.80%, p <0.001), showing, in subsequent occasions, similar to control negative. Multinucleated giant cells were found in areas of bone remodeling, with the Biogran® and test bioglass. BMP-2 levels in the negative control group were higher in 7 (418,80pg / ml, p =