Title: | Propriedades mecânicas de concretos autoadensável produzidos com nanotubos de carbono sintetizados diretamente sobre o clínquer |
Authors: | Laís Malta Coelho Silveira |
First Advisor: | José Márcio Fonseca Calixto |
First Co-advisor: | Luiz Orlando Ladeira |
First Referee: | Adriana Guerra Gumieri |
Second Referee: | Junia Nunes de Paula |
Third Referee: | Eduardo Chahud |
Abstract: | Pesquisas e estudos importantes vêm sendo desenvolvidos utilizando a nanotecnologia em materiais de construção. Desde a sua descoberta, os nanotubos de carbono (NTC) têm se mostrado capazes de potencializar compósitos em várias de suas propriedades e isto tem chamado a atenção para o uso dos NTC em matrizes cimentícias. Avanços na tecnologia do concreto têm permitido a melhoria de suas propriedades nos estados fresco e endurecido, pelo emprego de novos materiais e uso de novas técnicas. Nesse trabalho, concretos autoadensável (CAA) foram produzidos com nanotubos de carbono sintetizados diretamente sobre o clínquer. Parte do cimento utilizado na produção dos concretos foi substituída por clínquer nanoestruturado contendo diferentes teores de nanotubos de carbono (0,5%, 0,75% e 1% em relação à massa total de cimento anidro). Foram avaliadas a trabalhabilidade dos concretos no estado fresco e no estado endurecido as resistências à compressão e à tração por compressão diamentral bem como o módulo de elasticidade. O desempenho desses concretos foi comparado com um CAA de referência, sem nanotubos. Os resultados dos CAA estudados por Borges (2019), em sua pesquisa, também foram incluídos nessa análise. A avaliação dos resultados revela que CAA contendo teores de NTC acima de 0,5 % não apresentaram ganhos significativos de desempenho. Além disso, conclui-se que um possível teor ótimo de NTC a ser adicionado ao concreto autoadensável, para que o mesmo alcance seu melhor desempenho, esteja entre os teores de 0,30 e 0,50 % de NTC. |
Abstract: | Important research investigations have been developed using nanotechnologyin building materials. Since their discovery, carbon nanotubes (CNTs) have been able to improve composite material properties and this has drawn attention to the use of CNTs in cementitious matrices. Advances in concrete technology have allowed improved behavior in the fresh and hardened states employing new materials and techniques. In this work, self-compacting concretes (SCC) were produced with carbon nanotubes synthesized directly onthe clinker. Part of the cement used in the concrete production was replaced by nanostructured clinker containing different rates of carbon nanotubes (0.5%, 0.75%, and 1% of the cement mass). The workability of the SCC in the fresh state was evaluated and, in the hardened state, the compressive and splitting tensile strength as well as the modulus of elasticity. The behavior of these concretes was compared to a reference SCC, without carbon nanotubes. The results of the SCC investigated by Borges (2019) are also included in the analysis. The evaluation of the test results reveals that the SCC with NTC contents above 0.5% did not show any improvement in mechanical behavior. Besides, the results also show that the best performance of the investigated SCC was achieved for NTC content between 0.3 and 0.5 %. |
Subject: | Construção civil Materiais de construção Nanotubos de carbono Concreto |
language: | por |
metadata.dc.publisher.country: | Brasil |
Publisher: | Universidade Federal de Minas Gerais |
Publisher Initials: | UFMG |
metadata.dc.publisher.department: | ENG - DEPARTAMENTO DE ENGENHARIA MATERIAIS E DA CONSTRUÇÃO CIVIL |
metadata.dc.publisher.program: | Programa de Pós-Graduação em Construção Civil |
Rights: | Acesso Aberto |
URI: | http://hdl.handle.net/1843/44746 |
Issue Date: | 28-Sep-2020 |
Appears in Collections: | Dissertações de Mestrado |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
DissertaçãoFinal_LaísMaltaCoelhoSilveira.pdf | 2.58 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.