Título: | Ação do peróxido de hidrogênio a 35% sobre a microdureza de restaurações de resina composta a base de silorano |
Título(s) alternativo(s): | Action of 35% hydrogen peroxide on the microhardness of silorane composite resin restaurations |
Autor(es): | Bruna Costa Lage Ênio Lacerda Vilaça José Guilherme Férrer Pompeu Juvenil Alves Neves Diniz Ferreira Eduardo Lemos de Souza Rodrigo Richard da Silveira |
Resumen: | Objetivo: avaliar, in vitro, a ação de três diferentes clareadores a base de peróxido de hidrogênio a 35% sobre a microdureza Vickers (MV) de restaurações de resina composta a base de silorano. Material e mé-todos: a resina composta utilizada foi a FiltekTM P90 (3M) e os agentes clareadores: Whiteness HPTM (FGM), Whiteness HP MaxxTM (FGM) e Whiteness HP BlueTM (FGM). Foram preparados 10 espécimes de cada grupo, totalizando 40 corpos-de-prova, com auxílio de uma matriz bipartida de teflon. Os testes de microdureza foram realizados em-pregando-se um microdurômetro HMV-2T® (Shimadzu), e o cálculo foi obtido considerando-se as médias das quatro edentações de uma face. Os dados foram submetidos aos testes de análise de variância (ANOVA), usando um critério com o teste de Tukey. Para medida de significância estatística considerou-se p< 0,0001. Resultados: os valo-res médios e desvios padrão obtidos pelos grupos testados foram: G1: 49.500 (±5.1073); G2: 29.0685 (±4.9436); G3:28.7975 (±8.6736) e G4: 25.3535 (±9.4033). Houve diferença estatisticamente significativa entre os valores de MV quando comparado o grupo controle com os grupos experimentais. (p<0,0001). Entretanto, quando foram compa-radas os três grupos tratados com peróxido de hidrogênio, entre si, não houve diferença estatisticamente significante. Conclusão: o processo de oxidação e consequente degradação hidrolítica da resina compos-ta, na presença de peróxido de hidrogêno a 35%, levam a valores de microdureza menores e estatisticamente significantes |
Abstract: | Purpose: evaluate in vitro the action of three different bleaching with hydrogen peroxide at 35% on the Vickers hardness (MV) of composi-te restorations to silorane base. Methods: the composite resin used was the FiltekTM P90 (3M) and the bleaching were the Whiteness HPTM (FGM), Whiteness HP MaxxTM (FGM) e Whiteness HP BlueTM (FGM). Ten specimens of each group were prepared, totaling 40 specimens with the aid of a teflon bipartite matrix. The microhardness tests (MV) were performed employing a microhardness tester HMV-2T® (Shimadzu), and the calculation was obtained by considering the average of the four indentations of a face. The results were submitted to analysis of variance (ANOVA), using a criterion with the Tukey test. To measure statistical significance was considered p <0.0001. Results: the mean values and standard deviations obtained by the tested groups were: G1: 49.4500 (± 5.1073); G2: 29.0685 (± 4.9436); G3: 28.7975 (± 8.6736) and G4: 25.3535 (± 9.4033). There was a statistically significant differen-ce between the MV values when compared to the control group and experimental groups. (p <0.0001). However, when the three groups treated with hydrogen peroxide were compared with each other, the-re was no statistically significant difference. Conclusion: the oxidation process and subsequent hydrolytic degradation of the composite in the presence of hydrogen peroxide at 35% leads to lower but statisti-cally significant microhardeness values |
Asunto: | Peróxido de hidrogênio Resinas compostas Resinas de silorano Dureza |
Idioma: | por |
País: | Brasil |
Editor: | Universidade Federal de Minas Gerais |
Sigla da Institución: | UFMG |
Departamento: | FAO - DEPARTAMENTO DE ODONTOLOGIA RESTAURADORA FAO - DEPARTAMENTO DE ODONTOLOGIA SOCIAL E PREVENTIVA |
Tipo de acceso: | Acesso Aberto |
URI: | http://hdl.handle.net/1843/45460 |
Fecha del documento: | 2016 |
metadata.dc.url.externa: | https://periodicos.ufba.br/index.php/revfo/issue/view/1743 |
metadata.dc.relation.ispartof: | Revista da Faculdade de Odontologia da Universidade Federal da Bahia |
Aparece en las colecciones: | Artigo de Periódico |
archivos asociados a este elemento:
archivo | Descripción | Tamaño | Formato | |
---|---|---|---|---|
Ação do peróxido de hidrogênio a 35% sobre a microdureza de restaurações de resina composta a base de silorano.pdf | 217.68 kB | Adobe PDF | Visualizar/Abrir |
Los elementos en el repositorio están protegidos por copyright, con todos los derechos reservados, salvo cuando es indicado lo contrario.