| Título: | Long-term colloidal stability of graphene oxide aqueous nanofluids |
| Autor(es): | Jesús Andrés Nuncira Valencia Luciana Moreira Seara Rubén Dario Sinisterra Millán Vinicius Caliman Glaura Goulart Silva |
| Resumo: | The use of nanofluids for industrial applications depends on its stability during transport and use. In this work, we demonstrate that graphene oxide (GO)-based aqueous nanofluids can remaining stable for as many as 90 days. The structural and morphological analyses showed that the GO samples have an average thickness of two graphitic layers with interlayer spacing of 1 nm. The long-term colloidal stability of the nanofluids was monitored for 90 days using three different techniques: UV-vis, zeta potential (ζ) and DLS, which confirmed this stability. The observed ζ value (average of −64.8 ± 1.81 mV) at 200 ppm of GO is the highest negative value reported at pH = 4. The particle size distribution after 90 days of storage presented a major population with diameter of (530 ± 40) nm that represented 98% of the scattered light intensity. |
| Assunto: | Engenharia Química Nanotecnologia Materiais nanoestruturados Óxido de grafeno Microfluídica |
| Idioma: | eng |
| País: | Brasil |
| Editor: | Universidade Federal de Minas Gerais |
| Sigla da Instituição: | UFMG |
| Departamento: | CMI - CENTRO DE MICROSCOPIA ENG - DEPARTAMENTO DE ENGENHARIA QUÍMICA ICX - DEPARTAMENTO DE QUÍMICA |
| Tipo de Acesso: | Acesso Restrito |
| Identificador DOI: | https://doi.org/10.1080/1536383X.2019.1695250 |
| URI: | http://hdl.handle.net/1843/50891 |
| Data do documento: | 2020 |
| metadata.dc.url.externa: | https://www.tandfonline.com/doi/full/10.1080/1536383X.2019.1695250 |
| metadata.dc.relation.ispartof: | Fullerenes, Nanotubes and Carbon Nanostructures |
| Aparece nas coleções: | Artigo de Periódico |
Arquivos associados a este item:
Não existem arquivos associados a este item.
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.