Título: | Polyacrylamide copolymer/aminated carbon nanotube-based aqueous nanofluids for application in high temperature and salinity |
Autor(es): | Meiriane Cristina Faria Soares Lima Sthéfany Zaida Silva do Amparo Eder José Siqueira Douglas Rodrigues Miquita Vinicius Caliman Glaura Goulart Silva |
Resumen: | Polymer aqueous nanofluids have numerous industrial applications due to their synergic properties as a polymer and nanoparticle in the same fluid. The main goal of this work was to prepare stable aqueous nanofluids with improved viscosity in high temperature and salinity conditions. Aminated carbon nanotube (OCNT-TEPA) presented a C--N photoemission peak at 285.5 eV in X-ray photoelectron spectroscopy spectra, which is evidence of a grafting reaction. Fourier transform infrared spectra presented absorption bands attributed to amide and amine bonds. Elemental analyses showed 1.9 and 3.2 mass % N content increases for OCNT-TEPA and OCNT-TEPA-AM, respectively. Samples aged at 70 °C in brine confirmed that the addition of OCNT-TEPA increased the viscosity of nanofluids to 30% at day 90 compared to acrylamide–acrylic acid copolymer fluids. Nanotubes presented only 35% of the aminated functions compared to carbon black (Lima et al., Carbon 2016, 109, 209) , and their effects in the enhancement of viscosity and thermal and colloidal stability were 2× greater. |
Asunto: | Microscopia química Reologia Viscosidade Viscoelasticidade Nanotubos de carbono Copolímeros Poliacrilamida Nanopartículas Materiais nanoestruturados Termogravimetria Calorimetria Espectroscopia fotoeletonica Fourier, Espectroscopia de infravermelho por transformada de Microscopia eletronica |
Idioma: | eng |
País: | Brasil |
Editor: | Universidade Federal de Minas Gerais |
Sigla da Institución: | UFMG |
Departamento: | CMI - CENTRO DE MICROSCOPIA ICX - DEPARTAMENTO DE QUÍMICA |
Tipo de acceso: | Acesso Restrito |
Identificador DOI: | https://doi.org/10.1002/app.46382 |
URI: | http://hdl.handle.net/1843/51101 |
Fecha del documento: | jul-2018 |
metadata.dc.url.externa: | https://onlinelibrary.wiley.com/doi/10.1002/app.46382 |
metadata.dc.relation.ispartof: | Journal of Applied Polymer Science |
Aparece en las colecciones: | Artigo de Periódico |
archivos asociados a este elemento:
no existem archivos asociados a este elemento.
Los elementos en el repositorio están protegidos por copyright, con todos los derechos reservados, salvo cuando es indicado lo contrario.