Título: | Efeito da adição de magnetita em processo de polimerização de poli(estireno-co-divinilbenzeno) quanto à distribuição do tamanho de partículas |
Título(s) alternativo(s): | Effect of magnetite addition in poly(styrene-co-divinylbenzene) polymerization process on the particle size distribution |
Autor(es): | Mariana de Oliveira Reis Ricardo Geraldo de Sousa Adriana de Souza Medeiros Batista |
Resumo: | Os materiais poliméricos magnéticos possuem um vasto campo de aplicação devido às suas características, combinando as propriedades adsortivas com a facilidade de manipulação de suas partículas por meio de campos magnéticos externos. Neste trabalho, estudou-se o efeito da adição de magnetita [Fe3O4] para composição de poli(estireno-co-divinilbenzeno)/magnetita [StyDVB/Fe3O4] na homogeneidade obtida em termos de tamanho de partículas em comparação com o mesmo material sem o óxido de ferro. Para as polimerizações foram mantidas a relação de 4 % de DVB em volume de estireno utilizado, formando uma resina do tipo gel. As amostras foram caracterizadas por difração de laser e microscopia óptica. Foi realizado teste de intercâmbio iônico com as amostras após sulfonação utilizando NaOH 0,1 N, determinada por titulação com H2SO4 0,1 N (fenolftaleína como indicador), para se determinar a quantidade de íons trocados.Os resultados mostraram que o copolímero sem magnetita apresentou partículas mais uniformes e de maior diâmetro médio se comparado ao copolímero com magnetita. As imagens de microscopia óptica evidenciaram impacto na homogeneidade das partículas com a adição de Fe3O4, com formação de pequenos agregados, presença de gotículas laterais e esfericidade prejudicada. Teste de intercâmbio iônico evidenciou maior capacidade de adsorção pela amostra de Sty-DVB/Fe3O4. Os resultados contribuem para os esforços de composição de uma resina adsorvente com propriedades magnéticas, justificando a busca pela otimização do processo de síntese. |
Abstract: | Magnetic polymeric materials have a wide field of application due to their characteristics, combining adsorptive properties with the ease of handling their particles through external magnetic fields. In this work, the effect of adding magnetite [Fe3O4] to poly(styrene-codivinylbenzene)/magnetite [Sty-DVB/Fe3O4] composition on the homogeneity obtained in terms of particle size compared with the same material without the iron oxide was studied. For the polymerizations, the ratio of 4 % of DVB in volume of styrene used was maintained, forming a gel-like resin. The samples were characterized by laser diffraction and optical microscopy. Ion exchange test was performed with samples after sulfonation using 0.1 N NaOH, determined by titration with 0.1 N H2SO4 (phenolphthalein as indicator), to determine the amount of exchanged ions. The results showed that the copolymer without magnetite had more uniform particles and a larger average diameter compared to the copolymer with magnetite. Optical microscopy images showed impact on particle homogeneity with the addition of Fe3O4, with formation of small aggregates, presence of lateral droplets and impaired sphericity. Ion exchange test showed greater adsorption capacity by the Sty-DVB/Fe3O4 sample. The results contribute to the efforts to compose an adsorbent resin with magnetic properties, justifying the search for the optimization of the synthesis process. |
Assunto: | Estireno Óxido Ferroso-Férrico |
Idioma: | por |
País: | Brasil |
Editor: | Universidade Federal de Minas Gerais |
Sigla da Instituição: | UFMG |
Departamento: | ENG - DEPARTAMENTO DE ENGENHARIA QUÍMICA MED - DEPARTAMENTO DE ANATOMIA E IMAGEM |
Tipo de Acesso: | Acesso Aberto |
Identificador DOI: | 10.34117/bjdv7n10-160 |
URI: | http://hdl.handle.net/1843/57950 |
Data do documento: | 23-Nov-2021 |
metadata.dc.url.externa: | https://doi:10.34117/bjdv7n10-160 |
metadata.dc.relation.ispartof: | Brazilian Journal of Development |
Aparece nas coleções: | Artigo de Periódico |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Efeito da adição de magnetita em processo de polimerização de poli estireno-co-divinilbenzeno quanto à distribuição do tamanho de partículas pdfa.pdf | 383.83 kB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.