| Título: | Espalhamento ressonante de Raios-X aplicado ao estudo de nano-estruturas |
| Autor(es): | Leticia Goncalves Nunes Coelho |
| primer Tutor: | Rogerio Magalhaes Paniago |
| primer miembro del tribunal : | Ronald Dickman |
| Segundo miembro del tribunal: | Waldemar Augusto de Almeida Macedo |
| Tercer miembro del tribunal: | Richard Landers |
| Resumen: | Foram utilizadas técnicas de espalhamento ressonante de raios-X para estudar dois sistemas diferentes. Primeiramente, difração em incidência rasante associado às correções de dispersão no fator de espalhamento atômico foi utilizada para determinar o perfil de concentração química em ilhas auto-formadas de InP crescidas epitaxialmente em GaAs(001). A relaxação nas ilhas e a interdifusão de átomos do substrato nessas nanoestruturas foram determinadas para três amostras crescidas em temperaturas diferentes. Mapas de concentração em espaço real foram obtidos para duas amostras, que apresentavam apenas pontos coerentes. As ilhas crescidas em alta temperatura apresentaram alta concentração de átomos de Gálio, indicando forte desorção de átomos de Índio. Em seguida, espalhamento ressonante magnético na geometria de refletividade não-especular foi utilizado para determinar o comportamento magnético de um filme fino de MnAs crescido epitaxialmente sobre GaAs(001). A coexistência da fase ferromagnética com a fase paramagnética foi estudada em função da temperatura. A temperatura também influencia a configuração magnética do MnAs, que sofre uma reorganização dos domínios na fase ferromagnética em temperaturas mais altas. Observamos uma reorganização dos domínios magnéticos, que pode ser entendida levando-se em conta efeitos do campo demagnetizante na energia do sistema. Por fim, tirando proveito da seletividade química do espalhamento ressonante magnético, foi estudada uma bicamada magnética, consistindo de um filme de MnAs/GaAs(001) coberto por uma fina camada de Ferro. Os momentos magnéticos do filme de Ferro se alinham antiparalelamente ao filme de MnAs e também ao campo magnético externo aplicado numa certa faixa de temperatura. Este arranjo antiparalelo também está ligado ao campo demagnetizante do MnAs, que varia durante a coexistência de fases devido à variação da largura da fase ferromagnética. |
| Abstract: | In this thesis, resonant X-ray scattering techniques were used to study two different systems. First, grazing incidence difraction associated with dispersion corrections in the atomic scattering factor were employed to probe the chemical concentration profile in self-assembled islands of InP epitaxially grown on GaAs(001). The strain relaxation and substrate atoms diffusion were determined for three samples grown at different temperatures. Concentration maps in real space were obtained fortwo samples and showed high gallium interdiffusion in the islands grown at high temperature, indicating a high indium desorption rate.Next, magnetic resonant scattering in the non-specular reflectivity geometry was used to study the magnetic behavior of a thin MnAs film grown epitaxially on GaAs(001). Coexistence of the ferromagnetic and the paramagnetic phases was studied as function of temperature. The influence of temperature on the magnetic configuration on the MnAs was also addressed, and it was found that magnetic domain reconfiguration occurs at higher temperatures, within the MnAs ferromagnetic phase. This behavior is explained by the minimization of the energy term associated with the MnAs demagnetizing field. Finally, we took advantage of the chemical selectivity of resonant magnetic scattering to study separately a magnetic double layer composed of a MnAs film covered with a thin iron cap. Within a certain temperature range, the magnetic moments on the Fe layer align anti-parallel to the MnAs moments as well as to the applied external magnetic field. This anti-parallel ordering is also associated to the demagnetizing field of the MnAs layer, which varies within the phase coexistence range, due to the variable ferromagnetic phase width. |
| Asunto: | Nanoestruturas Raio-X Espalhamento Luz síncroton Espalhamento de ressonância Física |
| Idioma: | Português |
| Editor: | Universidade Federal de Minas Gerais |
| Sigla da Institución: | UFMG |
| Tipo de acceso: | Acesso Aberto |
| URI: | http://hdl.handle.net/1843/ESCZ-7N4HHY |
| Fecha del documento: | 10-abr-2008 |
| Aparece en las colecciones: | Teses de Doutorado |
archivos asociados a este elemento:
| archivo | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| leticia_coelho_tese.pdf | 6.82 MB | Adobe PDF | Visualizar/Abrir |
Los elementos en el repositorio están protegidos por copyright, con todos los derechos reservados, salvo cuando es indicado lo contrario.