ε-Martensite formation for low strains in a lean duplex stainless steel
Carregando...
Data
Título da Revista
ISSN da Revista
Título de Volume
Editor
Universidade Federal de Minas Gerais
Descrição
Tipo
Artigo de periódico
Título alternativo
Formação de ε-martensita para baixas deformações em um aço inoxidável lean duplex
Primeiro orientador
Membros da banca
Resumo
Martensitic transformation induced by strain in duplex stainless steels is a good option to increase their strength and elongation. The influence of low deformation levels on the phase transformation was studied in a 2304 lean duplex stainless steel. It was demonstrated that this steel exhibited the phase transformation of austenite (γ) into epsilon (ε) and alpha (α′) martensite after cold rolling. The ε and α′ were observed in shear bands and close to the grain boundaries. The Shoji–Nishiyama relation was observed. Hitherto, the ε formation has not been reported in the literature for this steel by cold deformation.
Abstract
A transformação martensítica induzida por deformação em aços inoxidáveis duplex é uma boa opção para aumentar sua resistência e alongamento. A influência de baixos níveis de deformação na transformação de fase foi estudada em um aço inoxidável 2304 lean duplex. Foi demonstrado que este aço apresentou a transformação de fase de austenita (γ) em épsilon (ε) e alfa (α′) martensita após a laminação a frio. Os ε e α' foram observados nas bandas de cisalhamento e próximo aos contornos de grão. A relação Shoji-Nishiyama foi observada. Até o momento, a formação ε não foi relatada na literatura para este aço por deformação a frio.
Assunto
Transformação de fases, ε-Martensite, Microestrutura, Aço inoxidável duplex, Laminação a frio