Title: | Avaliação do efeito do fator água/aglomerante em concreto de alto desempenho |
Authors: | Karla Ulisses Lima |
First Advisor: | Roberto Braga Figueiredo |
First Referee: | Roberto Braga Figueiredo |
Second Referee: | Augusta Cerceau Isaac Neta |
Third Referee: | Flávia Spitale Jacques Poggiali |
Abstract: | Concretos com resistências superiores ao concreto convencional tem sido alvo de pesquisas devido, principalmente, às propriedades associadas à durabilidade e desempenho mecânico. Para este tipo de concreto, alguns fatores devem ser minuciosamente analisados e empregados com eficiência, como por exemplo, a qualidade dos materiais utilizados, o método de mistura, o grau de adensamento, a porosidade, a quantidade de água utilizada, ou seja, fatores que podem afetar a resistência e a microestrutura do concreto. Este trabalho teve como objetivo verificar os efeitos da variação da relação água/aglomerante na resistência à compressão, porosidade e microestrutura de amostras de concreto desenvolvidas com traço de concreto de ultra-alto desempenho. O concreto foi desenvolvido com cimento Portland CP V, areia, pó de quartzo, sílica ativa, aditivo superplastificante e diferentes teores de água/aglomerante. As amostras foram caracterizadas por difração de raios-X e microscopia eletrônica de varredura e o volume de poros foi determinado pelo princípio de Arquimedes. A resistência mecânica foi verificada por meio do ensaio de resistência à compressão aos 7 e 28 dias. O concreto moldado com traço de concreto de ultra-alto desempenho foi considerado como concreto de alto desempenho devido à faixa de resistência apresentada que foi de 60 - 100 MPa. |
Abstract: | Concretes with higher strengths than conventional concrete have been the subject of research mainly due to properties associated with durability and mechanical performance. For these types of concrete, some factors must be throughly analyzed and used efficiently, such as the quality of the materials, the mixing method, the degree of density and porosity, the amount of water, that is, factors wich may affect the concrete strength and microstructure. This work aims to verify the effects of the water/binder ratio variation on the compressive strength, porosity and microstructure of concrete samples developed with the same composition as an ultra high performance concrete mix. The concrete was developed with Portland cement, sand, quartz powder, silica powder, superplasticizer and different water/binder ratios. The samples were characterized by X-ray diffraction, by scanning electron microscopy and pore volume. The mechanical strength was verified by compressive strength test at 7 and 28 days. The concret produced as an ultra high performance concrete mix was considered as high performance concrete due to the presented resistance range, 60 - 100 MPa. |
Subject: | Construção civil Materiais de construção Concreto Concreto - Durabilidade Microestrutura |
language: | por |
metadata.dc.publisher.country: | Brasil |
Publisher: | Universidade Federal de Minas Gerais |
Publisher Initials: | UFMG |
metadata.dc.publisher.department: | ENG - DEPARTAMENTO DE ENGENHARIA MATERIAIS E DA CONSTRUÇÃO CIVIL |
metadata.dc.publisher.program: | Programa de Pós-Graduação em Construção Civil |
Rights: | Acesso Aberto |
URI: | http://hdl.handle.net/1843/30128 |
Issue Date: | 10-Jul-2019 |
Appears in Collections: | Dissertações de Mestrado |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
DISSERTAÇÃO VERSÃO FINAL BIBLIOTECA - KARLA ULISSES LIMA.pdf | 1.66 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.