| Título: | Cytotoxicity, biocompatibility, and biomineralization of the new high-plasticity mta material |
| Autor(es): | Luciano Tavares Angelo Cintra Francine Benetti Índia Olinta de Azevedo Queiroz Juliana Maria de Araújo Lopes Sandra Helena Penha de Oliveira Gustavo Sivieri Araújo João Eduardo Gomes-Filho |
| Resumen: | Introduction: Mineral trioxide aggregate (MTA) has excellent biological properties, but its handling proper- ties have been criticized for both ProRoot MTA (Tulsa Dental Products, Tulsa, OK) and white MTA-Angelus (MTA-Ang; Angelus Ind ustria de Produtos Odon- tol ogicos S/A, Londrina, PR, Brazil). Angelus MTA HP (high plasticity) (Angelus Ind ustria de Produtos Odon- tol ogicos S/A) has been introduced recently. Considering the importance of biological properties of materials that will be in contact with the tissues, this study evaluated the cytotoxicity, biocompatibility, and biomineralization of MTA HP compared with white MTA-Ang. Methods: L929 fibroblast cell lines were cultured, and cell viability was assessed at 6, 24, 48, and 72 hours using the ala- mar Blue assay (Thermo Fisher Scientific, Waltham, MA). A subcutaneous implant test was performed with polyethylene tubes containing 1 of the materials or empty tubes (control) using 20 Wistar rats. After 7 and 30 days of implantation, the tubes with surrounding tis- sues were removed for analysis using hematoxylin-eosin or von Kossa stain or they remained unstained for obser- vation under polarized light. The results were statisti- cally analyzed (P < .05). Results: A significant increase in cell viability for MTA HP was observed after 24, 48, and 72 hours compared with the control (P < .05). At 72 hours, MTA HP exhibited a higher viability compared with white MTA-Ang (P < .05). His- tologic analysis performed at 7 days showed moderate inflammation and a thick fibrous capsule in all groups (P > .05). At 30 days, mild inflammation and a thin fibrous capsule were observed in all groups (P > .05). All materials had structures positive for von Kossa and birefringent to polarized light. Conclusions: MTA HP showed biocompatibility and biomineralization similar to MTA-Ang. In addition, MTA HP showed increased fibroblast cell viability compared with white MTA-Ang after a longer period |
| Asunto: | Materials testing Biomineralization |
| Idioma: | eng |
| País: | Brasil |
| Editor: | Universidade Federal de Minas Gerais |
| Sigla da Institución: | UFMG |
| Departamento: | FAO - DEPARTAMENTO DE ODONTOLOGIA RESTAURADORA |
| Tipo de acceso: | Acesso Restrito |
| Identificador DOI: | 10.1016/j.joen.2016.12.018 |
| URI: | http://hdl.handle.net/1843/45470 |
| Fecha del documento: | may-2017 |
| metadata.dc.url.externa: | https://www.sciencedirect.com/science/article/pii/S0099239916310640?via%3Dihub |
| metadata.dc.relation.ispartof: | Journal of Endodontics |
| Aparece en las colecciones: | Artigo de Periódico |
archivos asociados a este elemento:
no existem archivos asociados a este elemento.
Los elementos en el repositorio están protegidos por copyright, con todos los derechos reservados, salvo cuando es indicado lo contrario.