| Other Titles: | Pet-ol a new class of polyeses in the synthesis of polyurethanes |
| Authors: | Davi Pereira Rosa Araújo Luana Viana Araújo Renata Costa Silva Araújo Leonardo Giordano Paterno Alan Ribeiro Mól Vânya Márcia Duarte Pasa Breno Nonato de Melo |
| Abstract: | Uma nova classe de polióis foi preparada via glicerólise do PET (PET-ol), e empregada na síntese de poliuretanos (PU). Os PET-óis foram preparados a 240°C nos teores de 30, 40, 50%, sob catálise básica em 60 min de reação. Os PU’s foram formulados com os PET-óis reagidos com 4,4’-difenilmetano diisocianato (MDI) na razão NCO/OH=2, catalisada com dilaurato de dibutilestanho e água como agente de expansão. Os materiais foram caracterizados por FTIR, por TGA, teor de OH, acidez, por GPC e por densidade. A estabilidade térmica do PET-ol aumentou, com aumento do teor de PET. A eficiência da formação de novos polióis é observada nos espectros de FTIR, pelo surgimento e supressão de bandas características dos materiais de partida, gerando um poliéster polihidroxilado. Os PU’s apresentaram-se com ótima estabilidade dimensional e baixa densidade. A estabilidade térmica dos PU’s mostrou-se menor que a dos polióis, pois trata-se de natureza polimérica distinta, com menor grau de aromaticidade. |
| Abstract: | A new class of polyols was prepared via glycerolysis of PET (PET-ol) and used in the synthesis of polyurethanes (PU). The PET-ols were prepared at 240°C at the rates of 30, 40, 50%, under basic catalysis in 60 min of reaction. The PU's were formulated with PET-ols reacted with 4,4'-diphenylmethane diisocyanate (MDI) in the ratio NCO/OH = 2, catalyzed with dibutyltin dilaurate and water as blowing agent. The materials were characterized by FTIR, TGA, OH content, acidity, GPC and density. The thermal stability of PET-ol increased with increasing PET content. The efficiency of the formation of new polyols is observed in the FTIR spectra by the appearance and suppression of characteristic bands of the starting materials, generating a polyhydroxylated polyester. The PUs presented with great dimensional stability and low density. The thermal stability of PU’s was lower than that of polyols, because it is a distinct polymeric nature, with a lower degree of aromaticity. |
| Subject: | Polióis Espuma Polímeros Poliuretanas Garrafas PET Reciclagem Síntese |
| language: | por |
| metadata.dc.publisher.country: | Brasil |
| Publisher: | Universidade Federal de Minas Gerais |
| Publisher Initials: | UFMG |
| metadata.dc.publisher.department: | ICX - DEPARTAMENTO DE QUÍMICA |
| Rights: | Acesso Aberto |
| URI: | http://hdl.handle.net/1843/55552 |
| Issue Date: | 2019 |
| metadata.dc.url.externa: | http://e-democracia.com.br/cbpol/anais/2019/pdfs/plenary/4EGQ.pdf |
| metadata.dc.relation.ispartof: | Congresso Brasileiro de Polímeros |
| Appears in Collections: | Artigo de Evento |
Files in This Item:
| File | Description | Size | Format | |
|---|---|---|---|---|
| PET-ol uma nova classe de polióis na síntese de poliuretanos.pdf | 1.76 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.