| Título: | Análises de inclusões não metálicas no aço inoxidável ferrítico 409 |
| Autor(es): | Marcio Nascimento Cunha |
| primer Tutor: | Dagoberto Brandao Santos |
| primer miembro del tribunal : | Luiz Fernando Andrade de Castro |
| Segundo miembro del tribunal: | Tarcísio Reis de Oliveira |
| Resumen: | Inclusoes nao metalicas fazem parte do processo de producao do aco e e praticamente impossivel eliminar todas as inclusoes. Varios problemas, tanto de qualidade quanto operacionais na producao do aco, estao relacionados com estas inclusoes. O conhecimento das etapas do processo de fabricacao do aco, aliado a um metodo de caracterizacao, e um passo importante para se conhecer as possiveis fontes de inclusoes, o que auxilia no diagnostico de problemas e na determinacao rapida de solucoes. Tecnicas para obter inclusoes menos prejudiciais ao aco tem sido empregadas e a obtencao de inclusoes com ponto de fusao mais baixo apos tratamento com calcio tem semostrado efetivo. A proposta deste estudo foi obter a composicao quimica das inclusoes nao metalicas em cada etapa de producao do aco inoxidavel 409 na Aciaria, identificar as etapas de processo que mais afetam a limpidez da corrida, avaliar a evolucao das inclusoes ao longo dos processos e a possibilidade de modificacao das inclusoes com adicao de Ca-Si no Forno Panela. Amostragens do aco liquido e escoria foram realizadas em fases especificas durante a sua elaboracao em duas etapas. Na primeira etapa foi amostrada uma corrida com processo padrao e na segunda etapa foi amostrado umacorrida com adicao de Ca-Si no Forno Panela. Foram realizados exames no microscopio optico com analisador de imagem. As piores areas examinadas das amostras foram divididas em campos e todas as inclusoes nestes campos foram quantificadas. Inclusoes 2Zm foram caracterizadas em termos de composicao quimica no Microscopio Eletronico de Varredura com sistema EDS (MEV/EDS). Os resultados mostraram que a condicao de limpidez do aco 409 e mais afetada apos etapa de sopro no VOD, apos adicao de titanio no Forno Panela e no distribuidor do Lingotamento Continuo. A composicao quimica das principais inclusoes do tipo oxidos e modificada de acordo com os tratamentos empregados em cada processo e o efeito em obter inclusoes com baixo ponto de fusao com adicao de Ca-Si depende de variacoes de CaO nos oxidos em uma faixa muito estreita de dificil controle. |
| Abstract: | Non metallic inclusions make part of the steel production and are impossible to remove all of them. Several quality and operational problems in the production are linked with these inclusions. The knowledge about the process of production together a good investigationmethod is an important step to find the possible inclusions sources. It helps to problems analysis and to find solutions quickly. Some methods to obtain inclusion in order to improve the steel quality have been used. Inclusions with low melting point after calcium treatment have showed good results. The propose of this study was to obtain the chemical composition of the non metallic inclusions in specifics steps of production of the ferritic stainless steel 409 type in the Melt Shop, to identify the steps that effect the cleanness, to evaluate the inclusions constitution evolution during the process and to evaluate the possibility to modify the inclusions with calcium addition in the Ladle Furnace.Samples of the liquid steel and slag were taken in specifics process in two steps. In the first step samples were obtained from a standard heat and in the second one was used a heat with Ca-Si addition in the Ladle Furnace. Optical microscopy examination with image analyzer was carried out in the samples. The worst areas were divided by fields and every inclusion was quantified in these particular fields. Inclusions with size 2Zm had the chemical composition analyzed in a Scanning Electron Microscope with EDS (MEV/EDS). The results showed that the cleanness condition is more affected after the blowing step inthe VOD process, after titanium addition in the Ladle Furnace and in the tundish of the continuous casting. The chemical composition of the inclusions was changed according to the treatment in each process and the effect of the Ca-Si addition in order to obtain inclusions with low melting point depend on the CaO variation in a narrow range withdifficult control. |
| Asunto: | Engenharia metalúrgica |
| Idioma: | Português |
| Editor: | Universidade Federal de Minas Gerais |
| Sigla da Institución: | UFMG |
| Tipo de acceso: | Acesso Aberto |
| URI: | http://hdl.handle.net/1843/BUBD-AEAKX9 |
| Fecha del documento: | 3-dic-2015 |
| Aparece en las colecciones: | Dissertações de Mestrado |
archivos asociados a este elemento:
| archivo | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| disserta__o_m_rciocunha_final.pdf | 2.59 MB | Adobe PDF | Visualizar/Abrir |
Los elementos en el repositorio están protegidos por copyright, con todos los derechos reservados, salvo cuando es indicado lo contrario.