Title: Estudo da reologia e da microestrutura de pastas de cimento Portland com adição de nanosílica estabilizada
Authors: Suellen Mota Marques Costa
First Advisor: Adriana Guerra Gumieri
First Referee: Andréia Bicalho Henriques
Second Referee: Jose Marcio Fonseca Calixto
Third Referee: Elionai Cassiana de Lima Gomes
Abstract: Esta dissertação dedica-se ao estudo da reologia e da microestrutura de pastas de cimento Portland com adição de nanosílica estabilizada. O objetivoé investigar a influência da adição de nanosílica estabilizada na microestrutura de pastas de cimento Portland no estado endurecido, bem como a interferência dessa pozolana nas propriedades da pasta no estado fresco.Para estudo da reologia, avaliaramse parâmetros reológicos por meio dereometria. A seu turno, para avaliação da microestrutura das pastas no estado endurecido empregaram-se as técnicas da ressonância magnética nuclear no estado sólido (29Si NMR CP MAS), microscopia eletrônica de varredura (MEV) e difração de raios X (DRX). O estudo revelou que a adição de nanosílica estabilizada contribui para a redução dos parâmetros reológicos e consequente aumento da fluidez da pasta. No tocante à microestrutura, os efeitos foram mais significativos quando a nanosílica estabilizada foi empregada em conjunto com sílica ativa. Nesse caso, notou-se um efeito sinérgico entre as duas pozolanas, resultando em maior organização da microestrutura, bem como em cadeias mais longas de silicato de cálcio hidratado
Abstract: This work concernsthe study of rheology and microstructure of Portland cement pastes with stabilized nanosilica. The goal was toinvestigate the influence of stabilizednanosilica on microstructure of hard Portland cement pastes, as well as interferencesinfresh cement paste. For the rheology study, rheological parameters were evaluated by rheometry. In turn, the solid state nuclear magnetic resonance (29Si NMR CP MAS), scanning electron microscopy (SEM) and X-ray diffraction (XRD) techniques were used to evaluate the microstructure of hard paste. The study revealed that the addition of stabilized nanosilica contributes to the reduction of rheological parameters and consequent increase inflowability. Regarding the microstructure, the effects were more significant when stabilized nanosilica was used togheterwith silica fume. In this case, a synergistic effect was observed between thepozzolans, resulting in greater organization of the microstructure, as well as in longer calcium silicatehydrated chains
Subject: Reologia
Cimento Portland
Microestrutura
Construção civil
language: Português
Publisher: Universidade Federal de Minas Gerais
Publisher Initials: UFMG
Rights: Acesso Aberto
URI: http://hdl.handle.net/1843/BUOS-AWWLAU
Issue Date: 1-Jan-2017
Appears in Collections:Dissertações de Mestrado

Files in This Item:
File Description SizeFormat 
disserta__o_228.pdf25.37 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.