Please use this identifier to cite or link to this item:
http://hdl.handle.net/1843/ISMS-7RTNGX
Type: | Dissertação de Mestrado |
Title: | Estudo da influência do agregado graúdo de diferentes origens mineralógicas nas propriedades mecânicas do concreto |
Authors: | Miguel Fernando Schettini Alhadas |
First Advisor: | Jose Marcio Fonseca Calixto |
First Referee: | Adriano de Paula e Silva |
Second Referee: | Weber Guadagnin Morávia |
Third Referee: | Maria Cecilia Novaes Firmo Ferreira |
Abstract: | O principal objetivo do estudo foi avaliar a influência do agregado graúdo de diferentes origens mineralógicas nas propriedades mecânicas do concreto: resistência à compressão e módulo de deformação. Para isto foram produzidos concretos com quatro tipos deagregados: calcário, gnaisse, dolomito e basalto, perfazendo um total de seis amostras obtidas de seis cidades do Estado de Minas Gerais: duas amostras de agregado de calcário (Belo Horizonte e Montes Claros), duas amostras de agregado de gnaisse (Passos e Guaxupé), uma amostra de agregado de basalto (Uberlândia) e uma amostra de agregado de dolomito (Patos de Minas). No estudo foi utilizado um único lote de cimento do tipo CP III 40 RS, areia artificial quartzosa e um mesmo aditivo plastificante. Os concretos analisados foram especificados segundo a classe de agressividade II da NBR 6118:2003 que prescreve concreto com resistência característica à compressão (fck) mínima de 25,0 MPa e uma relação água/cimento 0,60. As propriedades mecânicas dos diversos concretos foram avaliadas nas idades de 3, 7, 14, 21 e 28 dias após a fabricação. Os resultados indicam um desempenho melhor dos concretos produzidos com agregado graúdo de dolomita e basalto. Uma boa correlação foi obtida entre os valores medidos do módulo de deformação para os diferentes concretos com os valores calculados pelas expressões sugeridas pela NBR 6118, ACI 318, EUROCODE 2 e CEB 1990. |
Abstract: | The goal of this study is to present the effects of the different types of coarse aggregate on the mechanical properties of concrete: compressive strength and secant modulus of elasticity (MOE). Limestone, gneiss, dolomite and basalt were used as coarse aggregates. These aggregates came from six different regions in the state of Minas Gerais. ABNT type CP III RS cement and natural sand, as fine aggregate, were employed in the fabrication of the concrete. The concrete mix proportion was based on environmental class II of NBR 6118: minimum characteristic compressive strength equal to 25 MPa and water cement ratio 0.60. The mechanical properties were evaluated 3, 7, 14, 21 and 28 days after casting the concrete. The test results indicate expressively the better performance of the concretes fabricated with dolomite and basalt aggregates. Good correlation was achieved between the measured MOE values for the different concretes with the values calculated employing expressions in terms of the compressive strength suggested by NBR 6118, ACI 318, EUROCODE 2 and CEB 1990. |
Subject: | Engenharia civil Agregados (Materiais de construção) Concreto Propriedades mecanicas Construção civil |
language: | Português |
Publisher: | Universidade Federal de Minas Gerais |
Publisher Initials: | UFMG |
Rights: | Acesso Aberto |
URI: | http://hdl.handle.net/1843/ISMS-7RTNGX |
Issue Date: | 29-Sep-2008 |
Appears in Collections: | Dissertações de Mestrado |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
estudo_da_influencia_do_agregado_graudo.pdf | 4.16 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.